What Are Stainless Steel 410 Bars?

Stainless Steel 410 Bars are high-strength corrosion-resistant rods produced from martensitic stainless steel alloy enriched with chromium and nickel, known for their exceptional strength in various industrial settings like aerospace and manufacturing where durability and dependability are key elements. Heat treatable with magnetic properties for added longevity under rigorous conditions Stainless Steel 410 Bars make an excellent addition for applications including shaft fasteners, fastener valves tooling components to provide long lasting performance under extreme conditions.

Stainless Steel 410 bars are widely recognized for their exceptional features and versatile applications across numerous industries. Composed mostly of iron, chromium and carbon with small amounts of other elements added in, these bars boast exceptional strength, durability and corrosion protection, making them popular choices in engineering and manufacturing environments.

410 Stainless Steel Bars

Stainless Steel 410 bars stand out for their impressive mechanical properties, such as hardness, toughness and tensile strength, making them suitable for applications which demand robustness and reliability. Their superior resistance to wear-and-abrasion also lends them well for use in harsh environments where friction or impact could occur, such as automotive components or industrial equipment parts prone to wearing and damage.

Stainless Steel 410 bars boast outstanding corrosion resistance in environments exposed to moisture, chemicals, and harsh conditions, such as marine environments or chemical processing plants where exposure occurs frequently. This remarkable feat of resistance is attributable to chromium's presence; this forms a protective oxide layer on their surfaces which inhibits rusting over time preventing further degradation; making these bars popularly utilized by marine environments, chemical processing plants, coastal structures requiring corrosion-resistance solutions.

Stainless Steel 410 bars not only possess outstanding mechanical and corrosion-resistance properties, but they are also known for their exceptional machinability and weldability. Their flexibility in fabrication processes facilitates quick shaping, cutting and joining to produce intricate components efficiently - an attribute invaluable in construction projects, architectural applications and fabrication workshops where customization and flexibility is of the utmost importance.

Stainless Steel 410 bars find widespread application in manufacturing products across industries. Their combination of strength, corrosion resistance and machinability has become popular for shafts, fasteners, valves, springs and fitting production as they offer increased machinability as well as strong reliability even under extreme temperatures and corrosion environments. They've even become the go-to material in aerospace defense for its exceptional reliability in extreme temperature environments or when exposed to hostile atmospheric environments like high temperatures or acid rain.

Pharmaceutical and food processing industries both heavily rely on stainless Steel 410 bars due to their hygienic properties and compliance with stringent regulatory standards. These bars are particularly advantageous when fabricating equipment and utensils used in producing pharmaceuticals, chemicals and consumable goods due to their inertness, easy cleaning processes and resistance against growth.

Apple Steels is a premier manufacturer and supplier of high-quality Stainless Steel 410 bars in Mumbai, India. Renowned for reliability and durability, our bars meet stringent industry standards making them suitable for various industrial applications. Trust us to bring quality products designed with precision.

Manufacturing Process Of Stainless Steel 410 Bars

Casting

Melting and Casting

Steel and alloying metals are loaded into an electric arc furnace. Once in the furnace, the metal is heated to a specific temperature above its melting point, usually in excess of 2800°F.

Forming Round Bar

Forming

Most cast steel is formed by hot rolling—the slab, bloom, or billet is heated and passed through large rollers, stretching out the steel into a longer, thinner form.

Heat Treatment

Heat treatment

Heat treatment strengthens rolled stainless steel by recrystallizing the deformed microstructure. Most stainless steel is heat treated by annealing.

Descaling

Descaling

A rolled piece of stainless steel acquires a layer of oxidized “mill scale,” which needs to be washed away to restore a shiny surface finish.

Cutting Round Bar

Cutting or Machining

Stainless steel is cut to a specified shape and size. The stainless steel can be sheared with circular knives, sawed with high-speed blades, or blanked with punches.

Specification Of SS 410 Rods

SS Bar Wire Standard ASTM A276 / A479, ASME SA276 / SA479
Stainless Steel Bar Dimensions EN, DIN, JIS, ASTM, BS, ASME, AISI
Stainless Steel Round bar size Diameter: 3-~800mm
Stainless Steel Hex Bar size 2-100mm A/F
SS Flat bar size Thickness: 2 -100mm
Width: 10 to 500mm
Stainless Steel Square bar size 4 to 100mm
SS Angle bar size 3mm*20mm*20mm~12mm*100mm*100mm
Hollow Bar 32mm OD x 16mm ID to 250mm OD x 200mm ID)
Stainless Steel Rectangular Size 33 x 30mm to 295 x 1066mm
SS Bars Finish Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black
SS Bar Tolerance H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements
Tempers Tempers range from dead soft annealed to ultra spring temper
Rolled Stainless Steel Flat Bars Condition Hardened & tempered, annealed
Cold Rolled Bar Technique Stainless Steel Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar, Rod
Stainless Steel Rounds Bar Form Round, Rod, T-Bar, Channel Bar, Precision Ground Bar, Flat Bar, Square, Blocks, Round Rod, Rings, Hollow, Triangle, Rectangle, Hex (A/F), Threaded, Half Round Bar, Profiles, Billet, Ingot, I/H Bar, Forging etc.

Types Of Stainless Steel 410 Bars, Round Bars

410 Stainless Steel Round Bar

Round Bar

410 Stainless Steel Hex Bar

Hexagonal Bar

410 Stainless Steel Square Bar

Square Bar

Other Types Of Stainless Steel 410 Rods

  • SS 410 Precision Round Bars
  • Stainless Steel 410 Polished Bar
  • UNS S41000 Bright Round Bars
  • 410 Stainless Steel Hot Rolled Bar
  • ASTM A276 SS 410 Forged Bar
  • UNS S41000 Round Bar
  • 410 SS Cold Drawn Bar
  • Stainless Steel 410 Forged Bar
  • SS 410 Rectangular Bar

Stainless Steel 410 Bars Equivalent Grades

STANDARD UNS WNR. JIS
SS 410 S41000 1.4550 SUS 410

Chemical Composition of SS 410 Bars

Grade C Mn Si P S Cr Ni
410 0.15 max 1.00 max 1.00 max 0.04 max 0.03 max min: 11.5
max: 13.5
0.50 max

Mechanical Properties of SS 410 Bars

Tensile Strength ksi (MPa) min Yield Strength 0.2% offset ksi (MPa) min Elongation (% in 50mm) min Hardness (Brinell) MAX Hardness (Rockwell B) MAX
65 (450) 30 (205) 20 217 96

Stainless Steel Bars Technical Information

SS 410 Rods Industrial Application

Electrical Industry

Automotive Industry

Construction Industry

Defence Industry

Pharmaceutical Industry

Petroleum Industry

Petrochemical Industry

Milk & Dairy Industry

Export & Supply Destination of SS 410 Bars

Austria, Azerbaijan, Belarus, Belgium, Bulgaria, Croatia, Cyprus, Czechia/Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Ireland, Italy, Latvia, Liechtenstein, Lithuania, Luxembourg, Malta, Moldova, Monaco, Netherlands, Norway, Poland, Portugal, Romania, Russia, Serbia, Slovakia, Spain, Sweden, Switzerland, Turkey, Ukraine, United Kingdom.

Afghanistan, Armenia, Azerbaijan, Bahrain, Bangladesh, Bhutan, British, China, Egypt, Hong Kong, India, Indonesia, Iran, Iraq, Israel, Japan, Jordan, Kuwait, Kyrgyzstan, Lebanon, Macau, Malaysia, Maldives, Mongolia, Myanmar, Nepal, North Korea, Oman, Philippines, Qatar, Russia, Saudi Arabia, Singapore, South Korea, Sri Lanka, Taiwan, Thailand, Turkey, United Arab Emirates, Vietnam.

Algeria, Angola, Botswana, Burkina Faso, Burundi, Cameroon, Central African Republic, Egypt, Eswatini, Ethiopia, Gambia, Kenya, Liberia, Libya, Madagascar, Mauritania, Mauritius, Morocco, Mozambique, Namibia, Niger, Nigeria, Rwanda, Senegal, Seychelles, South Africa, Tanzania, Tunisia, Uganda, Zambia, Zimbabwe.

Antigua and Barbuda, Bahamas, Barbados, Belize, Canada, Costa Rica, Cuba, Dominica, Dominican Republic, El Salvador, Grenada, Guatemala, Haiti, Honduras, Jamaica, Mexico, Nicaragua, Panama, Saint Lucia, Saint Vincent and the Grenadines, Trinidad and Tobago, United States of America, Argentina, Bolivia, Brazil, Chile, Colombia, Ecuador, Guyana, Paraguay, Peru, Suriname, Uruguay, Venezuela.